At Harsh Steel Nickel Alloy 200/UNS N02200 is available in Nickel Alloy 200 wire, Nickel Alloy 200 Round bar, Nickel Alloy 200 Forged bar, Nickel Alloy 200 hex bar, Nickel Alloy 200 Flat bar, Nickel Alloy 200 Circles, Nickel Alloy 200 Ring, Nickel Alloy 200 Tube, Nickel Alloy 200 seamless Pipe, Nickel Alloy 200 Welded / ERW Pipe, Nickel Alloy 200 Sheet, Nickel Alloy 200 Plate, Nickel Alloy 200 Coil, Nickel Alloy 200 Flanges, Nickel Alloy 200 fasteners, Nickel Alloy 200 Socket weld Fittings, Nickel Alloy 200 ferrule fittings, Nickel Alloy 200 Buttweld fittings Like cap, elbow, tee, Reducer.
Nickel Alloy 200 and Nickel Alloy 201 is solid solution strengthened, in a commercial sense pure wrought materials together with good mechanized properties in excess of a variety of temperature ranges and superb level of resistance to a lot of corrosives, specifically hydroxides. Nickel Alloy 201 ended up being a modification of 200 to overpower carbon and (. 02 max) which keeps this coming from becoming embrittled through intergranular precipitates at temperature ranges of 600° F to 1400° F in lots of procedures. Normally, your essential constraints of both equally, nickel 200 and nickel 201, are usually blended into just one, dual-certified chemistry resulting providing a one metal while using desired attributes of both equally precious metals, Nickel Alloy 200/201.
Nickel Alloy 200 and 201 deliver corrosion amount of resistance within lowering and simple advertising together with within oxidizing atmospheres provided that the actual oxidizing advertising makes it possible for the actual formation of a passive oxide film. This oxide film makes up about the actual components exceptional amount of resistance within caustic environments. Deterioration prices within both equally marine and rural atmospheres are incredibly low. The amount of resistance connected with Nickel Alloy 200 and 201 to be able to corrosion by distilled and normal seas is very useful. And yes it likewise offers exceptional support within going sea water actually at excessive pace, but in at standstill as well as very low-velocity sea water severe local episode may occur beneath fouling microorganisms as well as different remains. Within warm water devices in which the water is made up of fractional carbon and atmosphere using some size, corrosion prices will probably be at first excessive however will minimize eventually when conditions favor the actual formation of a protective film.
Nickel Alloy 200 is generally on a support at temps below 600° F. At increased temps Nickel Alloy 200 merchandise may have problems with graphitization which can result in severely compromised properties. Whenever functioning temps are hoped for to be able to exceed 600° F, carbon written content gets to be critical. The lower carbon written content connected with Nickel Alloy 201 tends to make the actual materials repellent to be able to graphitization and as a consequence fewer at the mercy of embrittlement. Nickel Alloy 200/201 are generally accepted with regard to structure connected with strain wrecks and elements beneath ASME Boiler and Pressure . Nickel Alloy 200 is usually accepted with regard to support up to 600° F though Nickel Alloy 201 is usually accepted with regard to support up to 1230° F. Reduction point is usually 2615-2635° F.
In what forms is Nickel Alloy 200/201 available at Harsh Steel?
What are the characteristics of Nickel Alloy 200/201?
Highly resistant to various reducing chemicals
|Nickel Alloy-200 Rod||ASTM B 160, ASME SB 160, DIN 17752, ISO 9723|
|Nickel Alloy-200 Bar||ASTM B 160, ASME SB 160, DIN 17752, ISO 9723|
|Nickel Alloy-200 Pipe||ASTM B 161, ASME SB161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, ASTM B 751, ASME B 751, ASTM B775, ASME SB 775, ASTM B 829, ASME SB 829 DIN 17751, ISO 6207|
|Nickel Alloy-200 Tube||ASTM B 161, ASME SB161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, ASTM B 751, ASME B 751, ASTM B775, ASME SB 775, ASTM B 829, ASME SB 829 DIN 17751, ISO 6207|
|Nickel Alloy-200 Plate||ASTM B 162, ASME SB 162, DIN 17750, ISO 6208|
|Nickel Alloy-200 Sheet||ASTM B 162, ASME SB 162, DIN 17750, ISO 6208|
|Nickel Alloy-200 Strip||ASTM B 162, ASME SB 162, DIN 17750, ISO 6208|
|Nickel Alloy-200 Fittings||ASTM B 366, ASME SB 366|
|Nickel Alloy-200 Forgings||ASTM B 546, ASME SB 564, ISO 9725, DIN 17754|
|Nickel Alloy-200 Wire||DIN 17753, ISO 9724|
|Nickel Alloy-200 Other/Similar Specs||UNS N02200, BS 3072, BS 3073, BS 3074, BS 3075, BS 3076, NA11, Werkstoff Nr. 2.4060, 2.4066, VNI200|
Stock availability of contact Sales
|Alloy Name||Trade Name||UNS No.||British Specs||American Specs||German Specs|
|Nickel Alloy 200||Nickel 200
|UNS N02200||BS 3072
Technical Data Sheet
|Chemical Composition Limits|
|Nickel Alloy 200||99.0 min||0.25 max||0.40 max||0.35 max||0.15 max||0.35 max||0.01 max|
|Nickel Alloy 201||99.0 min||0.25 max||0.40 max||0.35 max||0.02 max||0.35 max||0.01 max|
Typical Mechanical Properties
|Material||Tensile Strength||Yield Strength (0.2% Offset)||Elongation in 2" (%)||Hardness|
|ksi||MPa||ksi||MPa||Brinnell (3000kg)||Rockwell B|
|Nickel Alloy 200||55-75||380-520||15-30||105-210||55-40||90-120||45-70|
|Nickel Alloy 201||55-75||380-520||15-30||105-210||55-40||90-120||45-70|