Business Type : Manufacturer, Exporter, Supplier, Retailer
|Nickel Alloy-201 Rod||ASTM B 160, ASME SB 160, DIN 17752, ISO 9723|
|Nickel Alloy-201 Bar||ASTM B 160, ASME SB 160, DIN 17752, ISO 9723|
|Nickel Alloy-201 Pipe||ASTM B 161, ASME SB161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, ASTM B 751, ASME B 751, ASTM B775, ASME SB 775, ASTM B 829, ASME SB 829 DIN 17751, ISO 6207|
|Nickel Alloy-201 Tube||ASTM B 161, ASME SB161, ASTM B 163, ASME SB 163, ASTM B 725, ASME SB 725, ASTM B 730, ASME SB 730, ASTM B 751, ASME B 751, ASTM B775, ASME SB 775, ASTM B 829, ASME SB 829 DIN 17751, ISO 6207|
|Nickel Alloy-201 Plate||ASTM B 162, ASME SB 162, DIN 17750, ISO 6208|
|Nickel Alloy-201 Sheet||ASTM B 162, ASME SB 162, DIN 17750, ISO 6208|
|Nickel Alloy-201 Strip||ASTM B 162, ASME SB 162, DIN 17750, ISO 6208|
|Nickel Alloy-201 Fittings||ASTM B 366, ASME SB 366|
|Nickel Alloy-201 Forgings||ASTM B 546, ASME SB 564, ISO 9725, DIN 17754|
|Nickel Alloy-201 Wire||DIN 17753, ISO 9724|
|Nickel Alloy-201 Other/Similar Specs||UNS N02200, BS 3072, BS 3073, BS 3074, BS 3075, BS 3076, NA11, Werkstoff Nr. 2.4060, 2.4066, VNI200|
Preferred Buyer From
|Location||India, Kuwait, Oman, Saudi Arabia, Turkey|
At Harsh Steel Nickel Alloy 201 (UNS N02201) is available in Nickel Alloy 201 wire, Nickel Alloy 201 Round bar, Nickel Alloy 201 Forged bar, Nickel Alloy 201 hex bar, Nickel Alloy 201 Flat bar, Nickel Alloy 201 Circles, Nickel Alloy 201 Ring, Nickel Alloy 201 Tube, Nickel Alloy 201 seamless Pipe, Nickel Alloy 201 Welded / ERW Pipe, Nickel Alloy 201 Sheet, Nickel Alloy 201 Plate, Nickel Alloy 201 Coil, Nickel Alloy 201 Flanges, Nickel Alloy 201 fasteners, Nickel Alloy 201 Socket weld Fittings, Nickel Alloy 201 ferrule fittings, Nickel Alloy 201 Buttweld fittings Like cap, elbow, tee, Reducer.
Nickel Alloy 200 and Nickel Alloy 201 are solid solution strengthened, commercially pure wrought materials with good mechanical properties over a wide range of temperatures and excellent resistance to many corrosives, in particular hydroxides. Nickel Alloy 201 was a modification of 200 to control carbon (.02 max) which keeps it from being embrittled by intergranular precipitates at temperatures of 600° F to 1400° F in many processes. Typically, the elemental restrictions of both, nickel 200 and nickel 201, are combined into one, dual-certified chemistry resulting in a single alloy with the desired characteristics of both alloys, Nickel Alloy 200/201.
Nickel Alloy 200 and 201 deliver corrosion amount of resistance within lowering and simple advertising together with within oxidizing atmospheres provided that the actual oxidizing advertising makes it possible for the actual formation of a passive oxide film. This oxide film makes up about the actual components exceptional amount of resistance within caustic environments. Deterioration prices within both equally marine and rural atmospheres are incredibly low. The amount of resistance connected with Nickel Alloy 200 and 201 to be able to corrosion by distilled and normal seas is very useful. And yes it likewise offers exceptional support within going sea water actually at excessive pace, but in at standstill as well as very low-velocity sea water severe local episode may occur beneath fouling microorganisms as well as different remains. Within warm water devices in which the water is made up of fractional carbon and atmosphere using some size, corrosion prices will probably be at first excessive however will minimize eventually when conditions favor the actual formation of a protective film.
Nickel Alloy 200 hundred is generally on a support at temps below 600° F. At increased temps Nickel Alloy 200 hundred merchandise may have problems with graphitization which can result in severely compromised properties. Whenever functioning temps are hoped for to be able to exceed 600° F, carbon written content gets to be critical. The lower carbon written content connected with Nickel Alloy 201 tends to make the actual materials repellent to be able to graphitization and as a consequence fewer at the mercy of embrittlement. Nickel Alloy 200/201 are generally accepted with regard to structure connected with strain wrecks and elements beneath ASME Boiler and Pressure . Nickel Alloy 200 is usually accepted with regard to support up to 600° F though Nickel Alloy 201 is usually accepted with regard to support up to 1230° F. Reduction point is usually 2615-2635° F.
Nickel Alloy-201 (UNS N02201) is a commercially pure wrought nickel, with good mechanical properties and an excellent resistance to many corrosives. Nickel Alloy 201 has low carbon (0.02% max) for applications over 315°C it is mainly used for food processing equipment, chemical shipping drums, caustic handling equipment and piping, electronic parts, aerospace and missile components, rocket motor cases, magnetostrictive devices.
In what forms is Nickel Alloy 200/201 available at Harsh Steel?
What are the characteristics of Nickel Alloy 200/201?
Stock availability of contact Sales
|Alloy Name||Trade Name||UNS No.||British Specs||American Specs||German Specs|
|Nickel Alloy 201||Nickel 201||UNS N02201||BS 3072
AMS 5553 Sheet and Strip
Technical Data Sheet
|Chemical Composition Limits|
|Nickel Alloy 200||99.0 min||0.25 max||0.40 max||0.35 max||0.15 max||0.35 max||0.01 max|
|Nickel Alloy 201||99.0 min||0.25 max||0.40 max||0.35 max||0.02 max||0.35 max||0.01 max|
Typical Mechanical Properties
|Material||Tensile Strength||Yield Strength (0.2% Offset)||Elongation in 2"(%)||Hardness|
|ksi||MPa||ksi||MPa||Brinnell (3000kg)||Rockwell B|
|Nickel Alloy 200||55-75||380-520||15-30||105-210||55-40||90-120||45-70|
|Nickel Alloy 201||55-75||380-520||15-30||105-210||55-40||90-120||45-70|