Alloy 230 is a nickel-chromium-tungsten-molybdenum alloy that combines excellent high temperature strength, outstanding resistance to nitriding environments and excellent long term thermal stability. Haynes 230 is easily fabricated and has very good forming and welding characteristics. Due to Haynes 230 combined properties it is very well suited to a wide variety of component applications in the aerospace and power industries. Haynes 230 is used for combustion cans, transition ducts, flame holders, thermocouple sheaths and other important gas turbine components. Haynes alloy 230 is solution treated at 2150 to 2275°F followed by rapid cooling, and is supplied in this condition (as per AMS 5891 and AMS 5878). Haynes 230 can be both hot worked and cold worked and all parts should be annealed and rapidly cooled in order to restore the best balance properties.

Specifications

  • UNS N06230
  • AMS 5878 - Sheet, Strip and Plate
  • AMS 5891 - Bar and Forging
  • GE B50TF246
  • DIN 17744 No 2.4733
  • NiCr22W14Mo
  • ASME SB 435 Sheet, Strip and Plate
  • ASME SB 572 Bar and Rod
  • ASME SB 564 Forgings
  • ASME SB 619 Welding Pipe
  • ASME SB 622 Seamless Tube and Pipe
  • ASME SB 626 Welded Tube
  • ASME SB 366 Fittings
  • ASTM B435 Sheet, Strip and Plate
  • ASTM B572 Bar and Rod
  • ASTM B564 Forgings
  • ASTM B619 Welded Pipe
  • ASTM B 622 Seamless Tube and Pipe
  • ASTM B626 Welded Tube
  • ASTM B366 Fittings
  • Haynes 230
Read More...


Stock availability of contact Sales

Alloy Name Trade Name UNS No. American Specs German Specs French Specs
Nickel Alloy 230 Haynes 230 UNS N06230 AMS 5878 Sheet, Strip and Plate
AMS 5891 Bar and Forgings
DIN 17744 No 2.4733 NiCr22W14Mo

Technical Data Sheet

Chemical Composition Limits
Weight% C Mn Si P S Cr Co Fe Al Ti B Cu La W Mo Ni
Haynes 230 0.05-0.15 0.30-1.0 0.25-0.75 0.03 0.015 20.0-24.0 5 3 0.20-0.50 0.1 0.015 0.5 0.005-0.05 13.0-15.0 1.0-3.0 Rem

Typical Mechanical Properties

Material Test Temp °F Ultimate Tensile Strength 0.2 % Yield Strength Elongation in % Hardness HB
Haynes Alloy 230 Extruded Bar
Solution Treated (AMS 5891)
RT 758 Mpa 110 ksi 310 Mpa 45 ksi 35 241 max
Material Test Temp °F Ultimate Tensile Strength 0.2 % Yield Strength Elongation in % Hardness HB
Haynes Alloy 230 Sheet
Solution Treated (AMS 5878)
RT 793 Mpa
115 ksi
345 Mpa
50 ksi
40 25 max
Haynes Alloy 230 Sheet
Solution Treated (AMS 5878)
1000 699 Mpa
101.5 ksi
303 Mpa
44 ksi
53.7 -
Haynes Alloy 230 Sheet
Solution Treated (AMS 5878)
1400 539 Mpa
78.3 ksi
323 Mpa
46.9 ksi
61.2 -
Haynes Alloy 230 Sheet
Solution Treated (AMS 5878)
2000 90 Mpa
13.1 ksi
69 Mpa
10 ksi
37 -